An amorphous metal (also known as metallic glass or glassy metal) is a solid metallic material, usually an alloy, with disordered atomic-scale structure. Most metals are crystalline in their solid state, which means they have a highly ordered arrangement of atoms. Amorphous metals are non-crystalline, and have a glass-like structure. But unlike common glasses, such as window glass, which are typically electrical insulators, amorphous metals have good electrical conductivity. There are several ways in which amorphous metals can be produced, including extremely rapid cooling, physical vapor deposition, solid-state reaction, ion irradiation, and mechanical alloying. Previously, small batches of amorphous metals had been produced through a variety of quick-cooling methods, such as amorphous metal ribbons which had been produced by sputtering molten metal onto a spinning metal disk (melt spinning). The rapid cooling (in the order of millions of degrees Celsius a second) is too fast for crystals to form and the material is "locked" in a glassy state. Currently, a number of alloys with critical cooling rates low enough to allow formation of amorphous structure in thick layers (over 1 millimeter) have been produced; these are known as bulk metallic glasses (BMG). More recently, batches of amorphous steel with three times the strength of conventional steel alloys have been produced .
This article needs additional citations for verification. (April 2012) (Learn how and when to remove this template message)
The first reported metallic glass was an alloy (Au75Si25) produced at Caltech by W. Klement (Jr.), Willens and Duwez in 1960. This and other early glass-forming alloys had to be cooled extremely rapidly (on the order of one megakelvin per second, 106 K/s) to avoid crystallization. An important consequence of this was that metallic glasses could only be produced in a limited number of forms (typically ribbons, foils, or wires) in which one dimension was small so that heat could be extracted quickly enough to achieve the necessary cooling rate. As a result, metallic glass specimens (with a few exceptions) were limited to thicknesses of less than one hundred micrometers.
In 1976, H. Liebermann and C. Graham developed a new method of manufacturing thin ribbons of amorphous metal on a supercooled fast-spinning wheel. This was an alloy of iron, nickel, and boron. The material, known as Metglas, was commercialized in the early 1980s and is used for low-loss power distribution transformers (amorphous metal transformer). Metglas-2605 is composed of 80% iron and 20% boron, has Curie temperature of 373 °C and a room temperature saturation magnetization of 1.56 teslas.
In the early 1980s, glassy ingots with 5 mm diameter were produced from the alloy of 55% palladium, 22.5% lead, and 22.5% antimony, by surface etching followed with heating-cooling cycles. Using boron oxide flux, the achievable thickness was increased to a centimeter.[clarification needed]
Research in Tohoku University and Caltech yielded multicomponent alloys based on lanthanum, magnesium, zirconium, palladium, iron, copper, and titanium, with critical cooling rate between 1 K/s to 100 K/s, comparable to oxide glasses.[clarification needed]
In 1982, a study on amorphous metal structural relaxation indicated a relationship between the specific heat and temperature of (Fe0.5Ni0.5)83P17. As the material was heated up, the properties developed a negative relationship starting at 375 K, which was due to the change in relaxed amorphous states. When the material was annealed for periods from 1 to 48 hours , the properties developed a positive relationship starting at 475 K for all annealing periods, since the annealing induced structure disappears at that temperature. In this study, amorphous alloys demonstrated glass transition and a super cooled liquid region. Between 1988 and 1992, more studies found more glass-type alloys with glass transition and a super cooled liquid region. From those studies, bulk glass alloys were made of La, Mg, and Zr, and these alloys demonstrated plasticity even when their ribbon thickness was increased from 20 μm to 50 μm. The plasticity was a stark difference to past amorphous metals that became brittle at those thicknesses.
In 1988, alloys of lanthanum, aluminium, and copper ore were found to be highly glass-forming. Al-based metallic glasses containing Scandium exhibited a record-type tensile mechanical strength of about 1500 MPa.
Before new techniques were found in 1990, bulk amorphous alloys of several millimeters in thickness were rare, except for a few exceptions, Pd-based amorphous alloys had been formed into rods with a 2 mm diameter by quenching, and spheres with a 10 mm diameter were formed by repetition flux melting with B2O3 and quenching.
In the 1990s new alloys were developed that form glasses at cooling rates as low as one kelvin per second. These cooling rates can be achieved by simple casting into metallic molds. These "bulk" amorphous alloys can be cast into parts of up to several centimeters in thickness (the maximum thickness depending on the alloy) while retaining an amorphous structure. The best glass-forming alloys are based on zirconium and palladium, but alloys based on iron, titanium, copper, magnesium, and other metals are also known. Many amorphous alloys are formed by exploiting a phenomenon called the "confusion" effect. Such alloys contain so many different elements (often four or more) that upon cooling at sufficiently fast rates, the constituent atoms simply cannot coordinate themselves into the equilibrium crystalline state before their mobility is stopped. In this way, the random disordered state of the atoms is "locked in".
In 1992, the commercial amorphous alloy, Vitreloy 1 (41.2% Zr, 13.8% Ti, 12.5% Cu, 10% Ni, and 22.5% Be), was developed at Caltech, as a part of Department of Energy and NASA research of new aerospace materials.
In 2004, bulk amorphous steel was successfully produced by two groups: one at Oak Ridge National Laboratory, who refers to their product as "glassy steel", and the other at the University of Virginia, calling theirs "DARVA-Glass 101". The product is non-magnetic at room temperature and significantly stronger than conventional steel, though a long research and development process remains before the introduction of the material into public or military use.
In 2018 a team at SLAC National Accelerator Laboratory, the National Institute of Standards and Technology (NIST) and Northwestern University reported the use of artificial intelligence to predict and evaluate samples of 20,000 different likely metallic glass alloys in a year. Their methods promise to speed up research and time to market for new amorphous metals alloys.
This section needs additional citations for verification. (March 2019) (Learn how and when to remove this template message)
Amorphous metal is usually an alloy rather than a pure metal. The alloys contain atoms of significantly different sizes, leading to low free volume (and therefore up to orders of magnitude higher viscosity than other metals and alloys) in molten state. The viscosity prevents the atoms moving enough to form an ordered lattice. The material structure also results in low shrinkage during cooling, and resistance to plastic deformation. The absence of grain boundaries, the weak spots of crystalline materials, leads to better resistance to wear and corrosion. Amorphous metals, while technically glasses, are also much tougher and less brittle than oxide glasses and ceramics. Amorphous metals can be grouped in two categories, as either non-ferromagnetic, if they are composed of Ln, Mg, Zr, Ti, Pd, CA, Cu, Pt and Au, or ferromagnetic alloys, if they are composed of Fe, Co, and Ni. Thermal conductivity of amorphous materials is lower than that of crystalline metal. As formation of amorphous structure relies on fast cooling, this limits the maximum achievable thickness of amorphous structures.
To achieve formation of amorphous structure even during slower cooling, the alloy has to be made of three or more components, leading to complex crystal units with higher potential energy and lower chance of formation. The atomic radius of the components has to be significantly different (over 12%), to achieve high packing density and low free volume. The combination of components should have negative heat of mixing, inhibiting crystal nucleation and prolonging the time the molten metal stays in supercooled state.
The alloys of boron, silicon, phosphorus, and other glass formers with magnetic metals (iron, cobalt, nickel) have high magnetic susceptibility, with low coercivity and high electrical resistance. Usually the conductivity of a metallic glass is of the same low order of magnitude as of a molten metal just above the melting point. The high resistance leads to low losses by eddy currents when subjected to alternating magnetic fields, a property useful for e.g. transformer magnetic cores. Their low coercivity also contributes to low loss.
Amorphous metals have higher tensile yield strengths and higher elastic strain limits than polycrystalline metal alloys, but their ductilities and fatigue strengths are lower. Amorphous alloys have a variety of potentially useful properties. In particular, they tend to be stronger than crystalline alloys of similar chemical composition, and they can sustain larger reversible ("elastic") deformations than crystalline alloys. Amorphous metals derive their strength directly from their non-crystalline structure, which does not have any of the defects (such as dislocations) that limit the strength of crystalline alloys. One modern amorphous metal, known as Vitreloy, has a tensile strength that is almost twice that of high-grade titanium. However, metallic glasses at room temperature are not ductile and tend to fail suddenly when loaded in tension, which limits the material applicability in reliability-critical applications, as the impending failure is not evident. Therefore, there is considerable interest in producing metal matrix composites consisting of a metallic glass matrix containing dendritic particles or fibers of a ductile crystalline metal.
Perhaps the most useful property of bulk amorphous alloys is that they are true glasses, which means that they soften and flow upon heating. This allows for easy processing, such as by injection molding, in much the same way as polymers. As a result, amorphous alloys have been commercialized for use in sports equipment, medical devices, and as cases for electronic equipment.
Thin films of amorphous metals can be deposited via high velocity oxygen fuel technique as protective coatings.
Currently the most important application is due to the special magnetic properties of some ferromagnetic metallic glasses. The low magnetization loss is used in high efficiency transformers (amorphous metal transformer) at line frequency and some higher frequency transformers. Amorphous steel is a very brittle material which makes it difficult to punch into motor laminations. Also electronic article surveillance (such as theft control passive ID tags,) often uses metallic glasses because of these magnetic properties.
Amorphous metals exhibit unique softening behavior above their glass transition and this softening has been increasingly explored for thermoplastic forming of metallic glasses. Such low softening temperature allows for developing simple methods for making composites of nanoparticles (e.g. carbon nanotubes) and BMGs. It has been shown that metallic glasses can be patterned on extremely small length scales ranging from 10 nm to several millimeters. This may solve the problems of nanoimprint lithography where expensive nano-molds made of silicon break easily. Nano-molds made from metallic glasses are easy to fabricate and more durable than silicon molds. The superior electronic, thermal and mechanical properties of BMGs compared to polymers make them a good option for developing nanocomposites for electronic application such as field electron emission devices.
Ti40Cu36Pd14Zr10 is believed to be noncarcinogenic, is about three times stronger than titanium, and its elastic modulus nearly matches bones. It has a high wear resistance and does not produce abrasion powder. The alloy does not undergo shrinkage on solidification. A surface structure can be generated that is biologically attachable by surface modification using laser pulses, allowing better joining with bone.
Mg60Zn35Ca5, rapidly cooled to achieve amorphous structure, is being investigated, at Lehigh University, as a biomaterial for implantation into bones as screws, pins, or plates, to fix fractures. Unlike traditional steel or titanium, this material dissolves in organisms at a rate of roughly 1 millimeter per month and is replaced with bone tissue. This speed can be adjusted by varying the content of zinc.
Ti-based metallic glass, when made into thin pipes, have a high tensile strength of 2100 MPA, elastic elongation of 2% and high corrosion resistance. Using these properties, a Ti–Zr–Cu–Ni–Sn metallic glass was used to improve the sensitivity of a Coriolis flow meter. This flow meter is about 28-53 times more sensitive than conventional meters, which can be applied in fossil-fuel, chemical, environmental, semiconductor and medical science industry.
Zr-Al-Ni-Cu based metallic glass can be shaped into 2.2–5 mm by 4 mm pressure sensors for automobile and other industries, and these sensors are smaller, more sensitive, and possess greater pressure endurance compared to conventional stainless steel made from cold working. Additionally, this alloy was used to make the world's smallest geared motor with diameter 1.5mm and 9.9mm to be produced and sold at the time.
Modeling and theoryEdit
Bulk metallic glasses (BMGs) have now been modeled using atomic scale simulations (within the density functional theory framework) in a similar manner to high entropy alloys. This has allowed predictions to be made about their behavior, stability and many more properties. As such, new BMG systems can be tested, and tailored systems; fit for a specific purpose (e.g. bone replacement or aero-engine component) without as much empirical searching of the phase space and experimental trial and error.
- Some scientists only consider amorphous metals produced by rapid cooling from a liquid state to be glasses. Materials scientists commonly consider a glass to be any solid non-crystalline material, regardless of how it is produced.
- Ojovan, M. I.; Lee, W. B. E. (2010). "Connectivity and glass transition in disordered oxide systems". Journal of Non-Crystalline Solids. 356 (44–49): 2534. Bibcode:2010JNCS..356.2534O. doi:10.1016/j.jnoncrysol.2010.05.012.
- Klement, W.; Willens, R. H.; Duwez, POL (1960). "Non-crystalline Structure in Solidified Gold-Silicon Alloys". Nature. 187 (4740): 869–870. Bibcode:1960Natur.187..869K. doi:10.1038/187869b0.
- Libermann H. & Graham C. (1976). "Production Of Amorphous Alloy Ribbons And Effects Of Apparatus Parameters On Ribbon Dimensions". IEEE Transactions on Magnetics. 12 (6): 921. Bibcode:1976ITM....12..921L. doi:10.1109/TMAG.1976.1059201.
- Roya, R & Majumdara, A.K. (1981). "Thermomagnetic and transport properties of metglas 2605 SC and 2605". Journal of Magnetism and Magnetic Materials. 25 (1): 83–89. Bibcode:1981JMMM...25...83R. doi:10.1016/0304-8853(81)90150-5.
- Inoue, A. (2000). "Stabilization of metallic supercooled liquid and bulk amorphous alloys". Acta Materialia. 48: 279–306. CiteSeerX 10.1.1.590.5472. doi:10.1016/S1359-6454(99)00300-6.
- Chen, H. S.; Inoue, A.; Masumoto, T. (July 1985). "Two-stage enthalpy relaxation behaviour of (Fe0.5Ni0.5)83P17 and (Fe0.5Ni0.5)83B17 amorphous alloys upon annealing". Journal of Materials Science. 20 (7): 2417–2438. Bibcode:1985JMatS..20.2417C. doi:10.1007/BF00556071.
- Yokoyama, Yoshihiko; Inoue, Akihisa (2007). "Compositional Dependence of Thermal and Mechanical Properties of Quaternary Zr-Cu-Ni-Al Bulk Glassy Alloys". Materials Transactions. 48 (6): 1282–1287. doi:10.2320/matertrans.MF200622.
- Inoue, Akihisa; Zhang, Tao (1996). "Fabrication of Bulk Glassy Zr55Al10Ni5Cu30 Alloy of 30 mm in Diameter by a Suction Casting Method". Materials Transactions, JIM. 37 (2): 185–187. doi:10.2320/matertrans1989.37.185.
- Qin, C.L.; Zhang, W.; Zhang, Q.S.; Asami, K.; Inoue, A. (31 January 2011). "Chemical characteristics of the passive surface films formed on newly developed Cu–Zr–Ag–Al bulk metallic glasses". Journal of Materials Research. 23 (8): 2091–2098. doi:10.1557/JMR.2008.0284.
- Inoue, A.; Sobu, S.; Louzguine, D. V.; Kimura, H.; Sasamori, K. (2011). "Ultrahigh strength Al-based amorphous alloys containing Sc". Journal of Materials Research. 19 (5): 1539. Bibcode:2004JMatR..19.1539I. doi:10.1557/JMR.2004.0206.
- Chen, H.S; Turnbull, D (August 1969). "Formation, stability and structure of palladium-silicon based alloy glasses". Acta Metallurgica. 17 (8): 1021–1031. doi:10.1016/0001-6160(69)90048-0.
- Kui, H. W.; Greer, A. L.; Turnbull, D. (15 September 1984). "Formation of bulk metallic glass by fluxing". Applied Physics Letters. 45 (6): 615–616. Bibcode:1984ApPhL..45..615K. doi:10.1063/1.95330.
- Peker, A.; Johnson, W. L. (25 October 1993). "A highly processable metallic glass: Zr41.2Ti13.8Cu12.5Ni10.0Be22.5" (PDF). Applied Physics Letters. 63 (17): 2342–2344. Bibcode:1993ApPhL..63.2342P. doi:10.1063/1.110520.
- U.Va. News Service, "University Of Virginia Scientists Discover Amorphous Steel Material is three times stronger than conventional steel and non-magnetic" Archived 2014-10-30 at the Wayback Machine, U.Va. News Services, 7/2/2004
- Google Patents listing for Patent WO 2006091875 A2, "Patent WO 2006091875 A2 - Amorphous steel composites with enhanced strengths, elastic properties and ductilities (Also published as US20090025834, WO2006091875A3)", Joseph S Poon, Gary J Shiflet, Univ Virginia, 8/31/2006
- "Glassy Steel". ORNL Review. 38 (1). 2005. Archived from the original on 2005-04-08. Retrieved 2005-12-26.
- Ponnambalam, V.; Poon, S. J.; Shiflet, G. J. (2011). "Fe-based bulk metallic glasses with diameter thickness larger than one centimeter". Journal of Materials Research. 19 (5): 1320. Bibcode:2004JMatR..19.1320P. doi:10.1557/JMR.2004.0176.
- "Artificial intelligence accelerates discovery of metallic glass". Physorg. April 13, 2018. Retrieved 2018-04-14.
- Ren, Fang; Ward, Logan; Williams, Travis; Laws, Kevin J.; Wolverton, Christopher; Hattrick-Simpers, Jason; Mehta, Apurva (13 April 2018). "Accelerated discovery of metallic glasses through iteration of machine learning and high-throughput experiments". Science Advances. 4 (4): eaaq1566. Bibcode:2018SciA....4.1566R. doi:10.1126/sciadv.aaq1566. PMC 5898831. PMID 29662953.
- Gloriant, Thierry (2003). "Microhardness and abrasive wear resistance of metallic glasses and nanostructured composite materials". Journal of Non-Crystalline Solids. 316 (1): 96–103. Bibcode:2003JNCS..316...96G. doi:10.1016/s0022-3093(02)01941-5.
- Inoue, A.; Takeuchi, A. (April 2011). "Recent development and application products of bulk glassy alloys☆". Acta Materialia. 59 (6): 2243–2267. doi:10.1016/j.actamat.2010.11.027.
- Suryanarayana, C.; Inoue, A. (2011-06-03). Bulk Metallic Glasses. ISBN 978-1-4398-5969-8.[page needed]
- Russell, Alan & Lee, Kok Loong (2005). Structure-Property Relations in Nonferrous Metals. John Wiley & Sons. p. 92. Bibcode:2005srnm.book.....R. ISBN 978-0-471-70853-7.
- "Amorphous Alloy Surpasses Steel And Titanium". NASA. Retrieved 2018-09-19.
- Telford, Mark (2004). "The case for bulk metallic glass". Materials Today. 7 (3): 36–43. doi:10.1016/S1369-7021(04)00124-5.
- Ning, S. R.; Gao, J.; Wang, Y. G. (2010). "Review on Applications of Low Loss Amorphous Metals in Motors". Advanced Materials Research. 129-131: 1366–1371. doi:10.4028/www.scientific.net/AMR.129-131.1366.
- Saotome, Y.; Iwazaki, H. (2000). "Superplastic extrusion of microgear shaft of 10 μm in module". Microsystem Technologies. 6 (4): 126. doi:10.1007/s005420050180.
- Kumar, G.; Tang, H. X.; Schroers, J. (2009). "Nanomoulding with amorphous metals". Nature. 457 (7231): 868–872. Bibcode:2009Natur.457..868K. doi:10.1038/nature07718. PMID 19212407.
- Hojati-Talemi, Pejman (2011). "High performance bulk metallic glass/carbon nanotube composite cathodes for electron field emission". Applied Physics Letters. 99 (19): 194104. Bibcode:2011ApPhL..99s4104H. doi:10.1063/1.3659898.
- Maruyama, Masaaki (June 11, 2009). "Japanese Universities Develop Ti-based Metallic Glass for Artificial Finger Joint". Tech-on.
- "Fixing bones with dissolvable glass". Institute of Physics. October 1, 2009.
- Nishiyama, Nobuyuki; Amiya, Kenji; Inoue, Akihisa (October 2007). "Novel applications of bulk metallic glass for industrial products". Journal of Non-Crystalline Solids. 353 (32–40): 3615–3621. Bibcode:2007JNCS..353.3615N. doi:10.1016/j.jnoncrysol.2007.05.170.
- Nishiyama, N.; Amiya, K.; Inoue, A. (March 2007). "Recent progress of bulk metallic glasses for strain-sensing devices". Materials Science and Engineering: A. 449-451: 79–83. doi:10.1016/j.msea.2006.02.384.
- Inoue, A.; Wang, X.M.; Zhang, W. (2008). "Developments and applications of bulk metal glasses". Reviews on Advanced Materials Science. 18 (1): 1–9. CiteSeerX 10.1.1.455.4625.
- King, D.M.; Middleburgh, S.C.; Liu, A.C.Y.; Tahini, H.A.; Lumpkin, G.R.; Cortie, M. (January 2014). "Formation and structure of V–Zr amorphous alloy thin films" (PDF). Acta Materialia. 83: 269–275. doi:10.1016/j.actamat.2014.10.016. hdl:10453/41214.
- Middleburgh, S.C.; Burr, P.A.; King, D.M.; Edwards, L.; Lumpkin, G.R.; Grimes, R.W. (November 2015). "Structural stability and fission product behaviour in U3Si". Journal of Nuclear Materials. 466: 739–744. Bibcode:2015JNuM..466..739M. doi:10.1016/j.jnucmat.2015.04.052.
- Liquidmetal Design Guide
- "Metallic glass: a drop of the hard stuff" at New Scientist
- Glass-Like Metal Performs Better Under Stress Physical Review Focus, June 9, 2005
- "Overview of metallic glasses"
- New Computational Method Developed By Carnegie Mellon University Physicist Could Speed Design and Testing of Metallic Glass (2004) (the alloy database developed by Marek Mihalkovic, Michael Widom, and others)
- Telford, Mark (March 2004). "The case for bulk metallic glass". Materials Today. 7 (3): 36–43. doi:10.1016/S1369-7021(04)00124-5.
- New tungsten-tantalum-copper amorphous alloy developed at the Korea Advanced Institute of Science and Technology 
- Amorphous Metals in Electric-Power Distribution Applications
- Amorphous and Nanocrystalline Soft Magnets
- Kumar, Golden; Neibecker, Pascal; Liu, Yan Hui; Schroers, Jan (26 February 2013). "Critical fictive temperature for plasticity in metallic glasses". Nature Communications. 4 (1): 1536. Bibcode:2013NatCo...4E1536K. doi:10.1038/ncomms2546. PMC 3586724. PMID 23443564.
- "New metallic glass material created by starving it of nuclei". newatlas.com. Retrieved 2017-12-09.
- Metallic glasses and those composites, Materials Research Forum LLC, Millersville, PA, USA, (2018), p. 336 "Metallic Glasses and Their Composites". www.mrforum.com.