Did you know... that there are five main types of metalcasting defects: gas porosity, shrinkage defects, mold material defects, pouring metal defects, and metallurgical defects?
This article is within the scope of WikiProject Metalworking, a collaborative effort to improve the coverage of Metalworking on Wikipedia. If you would like to participate, please visit the project page, where you can join the discussion and see a list of open tasks.MetalworkingWikipedia:WikiProject MetalworkingTemplate:WikiProject MetalworkingMetalworking articles
This article is within the scope of WikiProject Chemistry, a collaborative effort to improve the coverage of chemistry on Wikipedia. If you would like to participate, please visit the project page, where you can join the discussion and see a list of open tasks.ChemistryWikipedia:WikiProject ChemistryTemplate:WikiProject ChemistryChemistry articles
This article has been given a rating which conflicts with the project-independent quality rating in the banner shell. Please resolve this conflict if possible.
Latest comment: 13 years ago2 comments2 people in discussion
Concepts to be explained: coherency point, 'molten steel qualities', rat tails, superheat. While I cleaned up the grammar, it is still confusing. —Preceding unsigned comment added by Anon423 (talk • contribs) 05:35, 23 July 2010 (UTC)
Also, primary and secondary cooling. --Anon423 (talk) 05:39, 23 July 2010 (UTC)Reply
Hi, thanks for the notes. I added a link to superheat, added a link to "primary and secondary cooling", and tried clarifying the "molten steel qualities" sentence to make it more understandable. As for rat tails, see [1]. The coherency point is as simple as it sounds: it's the point at which the metal stops flowing because the front solidified. Let me know if I can help in any other way. Wizard191 (talk) 12:40, 23 July 2010 (UTC)Reply
Latest comment: 13 years ago2 comments2 people in discussion
In an old book (I no longer have) I seem to remember that the term "coring" was used to describe "shrinkage cavities" - is this use of the term still used? If so the article Coring should be given a see also link to here. Thanks.Sf5xeplus (talk) 17:43, 8 March 2011 (UTC)Reply
Hrm, I did some research, but didn't come up with anything that supports that. That terminology would be very confusing because in casting the term "core" already has a specific meaning and in engineering it has the meaning of removing excess material from a casting or injection molding design. Wizard191 (talk) 22:02, 13 April 2011 (UTC)Reply