Disk read/write heads are the small parts of a disk drive which move above the disk platter and transform the platter's magnetic field into electrical current (read the disk) or, vice versa, transform electrical current into magnetic field (write the disk). The heads have gone through a number of changes over the years.
In a hard drive, the heads 'fly' above the disk surface with clearance of as little as 3 nanometres. The "flying height" is constantly decreasing to enable higher areal density. The flying height of the head is controlled by the design of an air-bearing etched onto the disk-facing surface of the slider. The role of the air bearing is to maintain the flying height constant as the head moves over the surface of the disk. If the head hits the disk's surface, a catastrophic head crash can result.
The heads themselves started out similar to the heads in tape recorders—simple devices made out of a tiny C-shaped piece of highly magnetizable material called ferrite wrapped in a fine wire coil. When writing, the coil is energized, a strong magnetic field forms in the gap of the C, and the recording surface adjacent to the gap is magnetized. When reading, the magnetized material rotates past the heads, the ferrite core concentrates the field, and a current is generated in the coil. In the gap the field is very strong and quite narrow. That gap is roughly equal to the thickness of the magnetic media on the recording surface. The gap determines the minimum size of a recorded area on the disk. Ferrite heads are large, and write fairly large features. They must also be flown fairly far from the surface thus requiring stronger fields and larger heads.
Metal in Gap (MIG)Edit
Metal in Gap (MIG) heads are ferrite heads with a small piece of metal in the head gap that concentrates the field. This allows smaller features to be read and written. MIG heads were replaced with thin film heads. Thin film heads were electronically similar to ferrite heads and used the same physics, but they were manufactured using photolithographic processes and thin films of material that allowed fine features to be created. Thin film heads were much smaller than MIG heads and therefore allowed smaller recorded features to be used. Thin film heads allowed 3.5 inch drives to reach 4GB storage capacities in 1995. The geometry of the head gap was a compromise between what worked best for reading and what worked best for writing.
The next head improvement was to optimize the thin film head for writing and to create a separate head for reading. The separate read head uses the magnetoresistive (MR) effect which changes the resistance of a material in the presence of magnetic field. These MR heads are able to read very small magnetic features reliably, but can not be used to create the strong field used for writing. The term AMR (Anisotropic MR) is used to distinguish it from the later introduced improvement in MR technology called GMR (giant magnetoresistance) and "TMR" (tunneling magnetoresistance). The introduction of the AMR head in 1990 by IBM led to a period of rapid areal density increases of about 100% per year. In 1997 GMR, giant magnetoresistive heads started to replace AMR heads.
Since 1990s, a number of studies have been done on the effects of colossal magnetoresistance (CMR), which may allow for even greater increases in density. But so far it has not led to practical applications because it requires low temperatures and large equipment size.
Tunneling magnetoresistance (TMR)Edit
In 2004, the first drives to use tunneling MR (TMR) heads were introduced by Seagate allowing 400 GB drives with 3 disk platters. Seagate introduced TMR heads featuring integrated microscopic heater coils to control the shape of the transducer region of the head during operation. The heater can be activated prior to the start of a write operation to ensure proximity of the write pole to the disk/medium. This improves the written magnetic transitions by ensuring that the head's write field fully saturates the magnetic disk medium. The same thermal actuation approach can be used to temporarily decrease the separation between the disk medium and the read sensor during the readback process, thus improving signal strength and resolution. By mid-2006 other manufacturers have begun to use similar approaches in their products.
Perpendicular magnetic recording (PMR)Edit
During the same time frame a transition to perpendicular magnetic recording (PMR) is occurring, in which for reasons of improved stability and higher areal density potential, the traditional in-plane orientation of magnetization in the disk is being changed to a perpendicular orientation. This has major implications for the write process and the write head structure, as well as for the design of the magnetic disk media or hard disk platter, less directly so for the read sensor of the magnetic head.
- Mee, C.; Daniel, Eric D. (1996). Magnetic recording technology. New York: McGraw-Hill. p. 7.1. ISBN 978-0-07-041276-7.
- "Read/Write Head Designs: Ferrite, Metal-In-Gap, And Thin-Film - Hard Drives 101: Magnetic Storage". Tom's Hardware. 2011-08-30. Retrieved 2019-04-13.
- Christopher H. Bajorek (November 2014). "Magnetoresistive (MR) Heads and the Earliest MR Head-Based Disk Drives: Sawmill and Corsair" (PDF). Computer History Museum, Mountain View, CA. Archived from the original (PDF) on 2015-12-20. Retrieved 2015-09-25.
- "Chemists exploring new material with 'next generation' computer hard drive possibilities". The University of Aberdeen News. 27 January 2014.
- Dagotto, Elbio (14 March 2013). "Brief Introduction to Giant Magnetoresistance (GMR)". Nanoscale Phase Separation and Colossal Magnetoresistance: The Physics of Manganites and Related Compounds. Springer Series in Solid-State Sciences. 136. Springer Science & Business Media. pp. 395–396. doi:10.1007/978-3-662-05244-0_21. ISBN 9783662052440.
- IWASAKI, Shun-ichi (February 2009). "Perpendicular magnetic recording—Its development and realization—". Proceedings of the Japan Academy. Series B, Physical and Biological Sciences. 85 (2): 37–54. doi:10.2183/pjab.85.37. ISSN 0386-2208.