The fineness of a precious metal object (coin, bar, jewelry, etc.) represents the weight of fine metal therein, in proportion to the total weight which includes alloying base metals and any impurities. Alloy metals are added to increase hardness and durability of coins and jewelry, alter colors, decrease the cost per weight, or avoid the cost of high-purity refinement. For example, copper is added to the precious metal silver to make a more durable alloy for use in coins, housewares and jewelry. Coin silver, which was used for making silver coins in the past, contains 90% silver and 10% copper, by mass. Sterling silver contains 92.5% silver and 7.5% of other metals, usually copper, by mass.
Various ways of expressing fineness have been used and two remain in common use: millesimal fineness expressed in units of parts per 1,000 and karats or carats used only for gold. Karats measure the parts per 24, so that 18 karat = 18⁄24 = 75% and 24 karat gold is considered 100% gold.
Millesimal fineness Edit
Millesimal fineness is a system of denoting the purity of platinum, gold and silver alloys by parts per thousand of pure metal by mass in the alloy. For example, an alloy containing 75% gold is denoted as "750". Many European countries use decimal hallmark stamps (i.e., "585", "750", etc.) rather than "14 k", "18 k", etc., which is used in the United Kingdom and United States.
It is an extension of the older karat system of denoting the purity of gold by fractions of 24, such as "18 karat" for an alloy with 75% (18 parts per 24) pure gold by mass.
The millesimal fineness is usually rounded to a three figure number, particularly where used as a hallmark, and the fineness may vary slightly from the traditional versions of purity.
Here are the most common millesimal finenesses used for precious metals and the most common terms associated with them.
- 999.5: what most dealers would buy as if 100% pure; the most common purity for platinum bullion coins and bars
- 999—three nines fine
- 950: the most common purity for platinum jewelry
- 900—one nine fine
- 999.999—six nines fine: The purest gold ever produced. Refined by the Perth Mint in 1957.
- 999.99—five nines fine: The purest type of gold currently produced; the Royal Canadian Mint regularly produces commemorative coins in this fineness, including the world's largest, at 100 kg.
- 999.9—four nines fine: Most popular. E.g. ordinary Canadian Gold Maple Leaf and American Buffalo coins.
- 999—24 karat, also occasionally known as three nines fine: e.g., Chinese Gold Panda coins.
- 995: The minimum allowed in Good Delivery gold bars.
- 990—two nines fine
- 986—Ducat fineness: Formerly used by Venetian and Holy Roman Empire mints; still in use in Austria and Hungary.
- 958.3—23 karat
- 916—22 karat: Crown gold. Historically the most widely used fineness for gold bullion coins, such as the oldest American Eagle denominations from 1795–1833. Currently used for British Sovereigns, South African Krugerrands, and the modern (1986—present) American Gold Eagles.
- 900—one nine fine: American Eagle denominations for 1837–1933; currently used in Latin Monetary Union mintage (e.g. French and Swiss "Napoleon coin" 20 francs).
- 899—American Eagles briefly for 1834—1836.
- 834—20 karat
- 750—18 karat: In Spain oro de primera ley (first law gold).
- 625—15 karat
- 585—14 karat
- 583.3—14 karat: In Spain oro de segunda ley (second law gold).
- 500—12 karat
- 417—10 karat: Lowest legal solid gold karat made in the US prior to the August 2018 revision of the FTC Guides (Now 1 karat is legal).
- 375—9 karat: Minimum standard for gold in somme of the Commonwealth realms: Australia, Canada, New Zealand, UK, etc. It is also the minimum in Austria, Ireland, Portugal and France.
- 333—8 karat: Minimum standard for gold in Germany after 1884. It is also the minimum for Denmark, Greece and Mexico.
- 1 karat: Legal minimum for gold in the US since the revision of the FTC Guides of August 2018.
- 999.99—five nines fine: The purest silver ever produced. This was achieved by the Royal Silver Company of Bolivia.
- 999.9—four nines fine: ultra-fine silver used by the Royal Canadian Mint for their Silver Maple Leaf and other silver coins
- 999—fine silver or three nines fine: used in Good Delivery bullion bars and most current silver bullion coins. Used in U.S. silver commemorative coins and silver proof coins starting in 2019.
- 980: common standard used in Mexico ca. 1930–1945
- 958: (23⁄24) Britannia silver
- 950: French 1st Standard
- 947.9: 91 zolotnik Russian silver
- 935: Swiss standard for watchcases after 1887, to meet the British Merchandise Marks Act and to be of equal grade to 925 sterling. Sometimes claimed to have arisen as a Swiss misunderstanding of the standard required for British sterling. Usually marked with three Swiss bears.
- 935: used in the Art Deco period in Austria and Germany. Scandinavian silver jewellers used 935 silver after the 2nd World War
- 925: (37⁄40) Sterling silver The UK has used this alloy from the early 12th century. Equivalent to plata de primera ley in Spain (first law silver)
- 917: a standard used for the minting of Indian silver (rupees), during the British raj and for some coins during the first Brazilian Republic.
- 916: 88 zolotnik Russian silver
- 900: one nine fine, coin-silver , or 90% silver: e.g. Flowing Hair and 1837–1964 U.S. silver coins. Also used in U.S. silver commemorative coins and silver proof coins 1982–2018.
- 892.4: US coinage 1485⁄1664 fine "standard silver" as defined by the Coinage Act of 1792: e.g. Draped Bust and Capped Bust U.S. silver coins (1795–1836)
- 875: 84 zolotnik is the most common fineness for Russian silver. Swiss standard, commonly used for export watchcases (also 800 and later 935).
- 835: A standard predominantly used in Germany after 1884, and for some Dutch silver; and for the minting of coins in countries of the Latin Monetary Union
- 833: (5⁄6) a common standard for continental silver especially among the Dutch, Swedish, and Germans
- 830: A common standard used in older Scandinavian silver
- 800: The minimum standard for silver in Germany after 1884; the French 2nd standard for silver; "plata de segunda ley" in Spain (second law silver); Egyptian silver; Canadian silver circulating coinage from 1920-1966/7
- 750: An uncommon silver standard found in older German, Swiss and Austro-Hungarian silver
- 720: Decoplata :many Mexican and Dutch silver coins use this standard, as well as some coins from Portugal's former colonies, Japan, Uruguay, Ecuador, Egypt, and Morocco.
- 600: Used in some examples of postwar Japanese coins, such as the 1957-1966 100 yen coin
- 500: Standard used for making British coinage 1920–1946 as well as Canadian coins from 1967-1968, and some coins from Colombia and Brazil.
- 400: Standard used for US half dollars between 1965 and 1970, and commemorative issue Eisenhower dollars between 1971 and 1978. Also used in some Swedish Krona coins.
- 350: Standard used for US Jefferson "war nickels" minted between 1942 and 1945.
The karat (US spelling, symbol k or Kt) or carat (UK spelling, symbol c or Ct) is a fractional measure of purity for gold alloys, in parts fine per 24 parts whole. The karat system is a standard adopted by US federal law.
- K = 24 × Mg / Mm
- K is the karat rating of the material,
- Mg is the mass of pure gold in the alloy, and
- Mm is the total mass of the material.
24-karat gold is pure (while 100% purity is very difficult to attain, 24-karat as a designation is permitted in commerce for a minimum of 99.95% purity), 18-karat gold is 18 parts gold, 6 parts another metal (forming an alloy with 75% gold), 12-karat gold is 12 parts gold (12 parts another metal), and so forth.
In England, the carat was divisible into four grains, and the grain was divisible into four quarts. For example, a gold alloy of 127⁄128 fineness (that is, 99.2% purity) could have been described as being 23-karat, 3-grain, 1-quart gold.
The karat fractional system is increasingly being complemented or superseded by the millesimal system, described above for bullion, though jewelry generally tends to still use the karat system.
Conversion between percentage of pure gold and karats:
- 58.33–62.50% = 14 k (acclaimed 58.33%)
- 75.00–79.16% = 18 k (acclaimed 75.00%)
- 91.66–95.83% = 22 k (acclaimed 91.66%)
- 95.83–99.95% = 23 k (acclaimed 95.83%)
- 99.95–100% = 24 k (acclaimed 99.95%)
However, this system of calculation gives only the mass of pure gold contained in an alloy. The term 18-karat gold means that the alloy's mass consists of 75% of gold and 25% of other metals. The quantity of gold by volume in a less-than-24-karat gold alloy differs according to the alloys used. For example, knowing that standard 18-karat yellow gold consists of 75% gold, 12.5% silver and the remaining 12.5% of copper (all by mass), the volume of pure gold in this alloy will be 60% since gold is much denser than the other metals used: 19.32 g/cm3 for gold, 10.49 g/cm3 for silver and 8.96 g/cm3 for copper.
This formula gives the amount of gold in cubic centimeters or in milliliters in an alloy:
- VAu is the volume of gold in cubic centimeters or in milliliters
- Ma is the total mass of the alloy in grams
- kt is the karat purity of the alloy
To have the percentage of the volume of gold in an alloy, divide the volume of gold in cubic centimeters or in milliliters by the total volume of the alloy in cubic centimeters or in milliliters.
For 10-carat gold, the gold volume in the alloy represents about 26% of the total volume for standard yellow gold.
Karat is a variant of carat. First attested in English in the mid-15th century, the word carat came from Middle French carat, in turn derived either from Italian carato or Medieval Latin carratus. These were borrowed into Medieval Europe from the Arabic qīrāṭ meaning "fruit of the carob tree", also "weight of 5 grains", (قيراط) and was a unit of mass though it was probably not used to measure gold in classical times. The Arabic term ultimately originates from the Greek kerátion (κεράτιον) meaning carob seed (literally "small horn") (diminutive of κέρας – kéras, "horn").
In 309 CE, Roman Emperor Constantine I began to mint a new gold coin solidus that was 1⁄72 of a libra (Roman pound) of gold equal to a mass of 24 siliquae, where each siliqua (or carat) was 1⁄1728 of a libra. This is believed to be the origin of the value of the karat.
Verifying fineness Edit
While there are many methods of detecting fake precious metals, there are realistically only two options available for verifying the marked fineness of metal as being reasonably accurate: assaying the metal (which requires destroying it), or using X-ray fluorescence (XRF). XRF will measure only the outermost portion of the piece of metal and so may get misled by thick plating.
That becomes a concern because it would be possible for an unscrupulous refiner to produce precious metals bars that are slightly less pure than marked on the bar. A refiner doing $1 billion of business each year that marked .980 pure bars as .999 fine would make about an extra $20 million in profit. In the United States, the actual purity of gold articles must be no more than .003 less than the marked purity (e.g. .996 fine for gold marked .999 fine), and the actual purity of silver articles must be no more than .004 less than the marked purity.
Fine weight Edit
A piece of alloy metal containing a precious metal may also have the weight of its precious component referred to as its "fine weight". For example, 1 troy ounce of 18 karat gold (which is 75% gold) may be said to have a fine weight of 0.75 troy ounces.
Most modern government-issued bullion coins specify their fine weight. For example, the American Gold Eagle is embossed One Oz. Fine Gold and weighs 1.091 troy oz.
Troy mass of silver content Edit
Fineness of silver in Britain was traditionally expressed as the mass of silver expressed in troy ounces and pennyweights (1⁄20 troy ounce) in one troy pound (12 troy ounces) of the resulting alloy. Britannia silver has a fineness of 11 ounces, 10 pennyweights, or about silver, whereas sterling silver has a fineness of 11 ounces, 2 pennyweights, or exactly silver.
See also Edit
- London Bullion Market Association. "Definitions". Archived from the original on 2015-07-12.
- Seyd, Ernest (1868). Bullion and foreign exchanges theoretically and practically considered. E. Wilson. p. 146. Retrieved 21 March 2012.
- "The Perth Mint :: History". Gold Corporation. Archived from the original on 2011-05-14. Retrieved 2011-05-08.
- Thomas, Athol. 90 Golden Years, The story of the Perth Mint. Gold Corporation. p. 58.
- Royal Canadian Mint. "The Million Dollar Coin – a true milestone in minting". Archived from the original on 9 March 2015. Retrieved 13 July 2017.
In October 2007, the Million Dollar Coin was certified by Guinness World Records to be the world's largest gold coin.
- "Fineness of Gold". Gold Rate for Today. Archived from the original on August 7, 2013. Retrieved 2013-08-15.
- "..:: Royal Silver Company ::." Archived from the original on 2013-03-16.
- U.S. Mint abandons 90 percent silver composition
- "Silver standards". Antiques in Oxford. Retrieved 2020-10-05.
- "Canadian Coin Melt Values - Coinflation". www.coinflation.com. Archived from the original on 2017-06-17. Retrieved 2017-11-12.
- "Decoplata: The History of .720 Silver in World Coinage". 18 January 2022.
- "10 Escudos, Angola". en.numista.com. Retrieved 2021-11-04.
- "10 Sen - Taishō, Japan". en.numista.com. Retrieved 2021-11-13.
- "1 Peso, Uruguay". en.numista.com. Retrieved 2021-11-04.
- Melaragno, Michele. The VNR Dictionary of Engineering Units and Measures. Van Nostrand Reinhold. p. 114.
- The VNR OXFORD Dictionary for Scientific Writers and Editors. Oxford University Press. p. 56.
- "United States Code, 16 CFR 23.3 - Misrepresentation as to gold content". Archived from the original on 2017-02-14.
- Comprehensive Jewelry Precious Metals Overview Archived 2015-02-17 at the Wayback Machine International Gem Society (IGS), Retrieved 01-16-2015
- carat Archived 2010-10-24 at the Wayback Machine, Oxford Dictionaries
- Harper, Douglas. "carat". Online Etymology Dictionary.
- κεράτιον Archived 2012-10-08 at the Wayback Machine, Henry George Liddell, Robert Scott, A Greek-English Lexicon, on Perseus
- Walter W. Skeat (1888), An Etymological Dictionary of the English Language
- κέρας Archived 2012-10-08 at the Wayback Machine, Henry George Liddell, Robert Scott, A Greek-English Lexicon, on Perseus
- Vagi, David L. (1999). Coinage and History of the Roman Empire. Vol. II: Coinage. Chicago: Fitzroy Dearborn. p. 100. ISBN 978-1-57958-316-3. Archived from the original on 7 June 2013. Retrieved 18 November 2011.
- Grierson, Philip (1968). Catalogue of the Byzantine Coins in the Dumbarton Oaks Collection and in the Whittemore Collection. Vol. 2: pt. 1. Washington, DC: Dumbarton Oaks. p. 8. ISBN 978-0-88402-024-0. Archived from the original on 6 June 2013. Retrieved 18 November 2011.
- Turnbull, L. A.; Santamaria, L.; Martorell, T.; Rallo, J.; Hector, A. (2006). "Seed size variability: From carob to carats". Biology Letters. 2 (3): 397–400. doi:10.1098/rsbl.2006.0476. PMC 1686184. PMID 17148413.
- "15 U.S. Code Chapter 8 - FALSELY STAMPED GOLD OR SILVER OR GOODS MANUFACTURED THEREFROM". Archived from the original on 2016-11-07.
- The dictionary definition of fineness at Wiktionary
- Turnbull, Lindsay A; et al. (Oct 2006). "Seed size variability: From carob to carats". Biology Letters. 2 (3): 397–400. doi:10.1098/rsbl.2006.0476. PMC 1686184. PMID 17148413.
in a perception experiment observers could discriminate differences in carob seed weight of around 5% by eye... suggesting that human rather than natural selection gave rise to the carob myth