A release agent (also mold release agent, release coating, or mold release coating) is a chemical used to prevent other materials from bonding to surfaces. It can provide a solution in processes involving mold release, die-cast release, plastic release, adhesive release, and tire and web release.
Release agents provide the critical barrier between a molding surface and the substrate, facilitating separation of the cured part from the mold. Without such a barrier in place, the substrate would become fused to the mold surface, resulting in difficult clean-up and dramatic loss in production efficiency. Even when a release agent is used, factors such as irregular applications or improper release agent choice may have a dramatic effect on the quality and consistency of the finished product.
- 1 Types of Release Agents
- 2 Applications
- 3 References
Types of Release AgentsEdit
This section does not cite any sources. (October 2018) (Learn how and when to remove this template message)
One of the key attributes of a release agent is its degree of permanence: how long will it last before reapplication is necessary. A semi-permanent release agent does not need to be reapplied for every cycle of a molding operation and even works better when it is not over-applied to the mold surface.
How many releases can be achieved before reapplication is necessary varies by process, material, and application method. In order to achieve multiple releases per application, the semi-permanent release coating generally must be applied to a clean, dry surface free of dirt, rust, grime or previous coatings. This allows the release agent to properly bond to the mold and mold tooling, improving durability and longevity of the coating.
Sacrificial coatings must be applied before every cycle of a molding operation and are therefore considered more labor intensive. Most molders will prefer semi-permanent coatings to sacrificial coatings, especially when molding rubber and plastic parts. These coatings contain fewer solid ingredients, and thus do not last as long as semi-permanent coatings.
Water or Solvent-basedEdit
Release agents may be water or solvent-based and use of either will depend on the personal preference of the molder, plant safety regulations, hazardous materials shipping costs, state, local, or federal regulations, and/or desired drying times of the release coating.
Water-based release coatings generally dry slower than solvent-based release agents but present fewer health and safety concerns. Water-based release agents will be less expensive to ship because of their inherently non-flammable nature and satisfy most plant-safety goals.
Solvent-based release coatings dry almost instantly but present serious health and safety concerns. Fumes from solvent-based release agents may be hazardous without proper ventilation of the work area. Most solvents used in release agents are flammable.
Non-flammable release agents are available and usually classified as combustible.
Asphalt Release Agents are chemical products developed and manufactured as alternatives to diesel and solvents commonly used for cleaning equipment associated with Hot Mix Asphaltic Concrete (HMAC) production and placement on government and private facilities. The United States Oil Pollution Act of 1980 was used as the foundation to build the current program. The intent of asphalt release agents is to eliminate harmful stripping products that come into contact with bituminous products and strip the asphalt (binding agent) from the aggregates causing potholes, raveling, and other detrimental pavement failures.
In the concrete construction industry, form release agents prevent the adhesion of freshly placed concrete to the forming surface, usually plywood, overlaid plywood, steel or aluminum. In this application, there are two types of release agents available: barrier and reactive.
Reactive release agents are chemically active and work by the process of a chemical reaction between the release agent and the free limes available in fresh concrete. A soapy film is created which prevents adhesion. Because it is a chemically reactive process, there is generally little to no residue or non-reacted product left on the forming surface or concrete which provides for a cleaner process.
Release agents are used to aid in the separation of food from a cooking container after baking or roasting. Traditionally fat or flour have been used, but in industrial food processing other chemicals might be used. The application is called bakery release.
Mold release agent also can be used in die casting or metal forging process of metal, such as Aluminum, Aluminum Alloy, Zinc, Zinc Alloy, Magnesium, etc.
In industrial papermaking release agents are used to get slip effect of the paper from the processing equipment. A release agent may be applied on the process rolls (like the yankee dryer) or in the paper coating.
- Release liners for pressure-sensitive adhesive laminates and tapes
- Casting papers
- General industrial release papers
- Food-grade release and packaging papers
Release agents (e.g., magnesium stearate) are added to powdered and granulated drug compositions, to serve as a lubricant for mold release purposes during tabletting.
Release agents are coated onto some plastic films to prevent adhesives from bonding to the plastic surface. Some release agents, also known as de-molding agent, form oil, parting agent or form releaser, are substances used in molding and casting that aid in the separation of a mould from the material being moulded and reduce imperfections in the moulded surface.
There are two types of release agents used in the molding of rubber products. Both are silicone based. The decision on which to use has to do with lubricity and release. Water-diluted silicon is used when you have rubber sliding over a hot mold (sheets or slugs). The silicon keeps the rubber from sticking to the mold but just as important it lubricates the rubber so it will slide over the hot mold as it is loaded. Diluted silicon typically has to be applied every cycle. Semi-permanent mold release builds a silicon matrix on the mold that becomes a barrier between the rubber and the metal surface of the mold. The matrix is created by the other ingredients in the semi-permanent mold release. Applications of semi-permanent mold release vary from every cycle to once daily applications depending on the compound being molded and the design and quality of the mold. Silicone-based rubber products, however, require a non-silicone based releasing agent.