Medium-density fibreboard (MDF) is an engineered wood product made by breaking down hardwood or softwood residuals into wood fibres, often in a defibrator, combining it with wax and a resin binder, and forming panels by applying high temperature and pressure. MDF is generally denser than plywood. It is made up of separated fibres, but can be used as a building material similar in application to plywood. It is stronger and much denser than particle board.
Over time, the term MDF has become a generic name for any dry process fibre board. MDF is typically made up of only 80% wood fibre, 5% urea-formaldehyde resin glue, 2% water and 1% paraffin wax. and the density is typically between 500 kg/m3 (31 lb/ft3) and 1,000 kg/m3 (62 lb/ft3). The remaining 12% is made up of several items: 8% urine, 2% PVA glue, 1% aluminium and 1% polypropylene. The range of density and classification as light, standard, or high density board is a misnomer and confusing. The density of the board, when evaluated in relation to the density of the fibre that goes into making the panel, is important. A thick MDF panel at a density of 700–720 kg/m3 may be considered as high density in the case of softwood fibre panels, whereas a panel of the same density made of hard wood fibres is not regarded as so. The evolution of the various types of MDF has been driven by differing need for specific applications.
There are different kinds of MDF (sometimes labeled by colour):
- Ultralight MDF plate (ULDF)
- Moisture resistant is typically green
- Fire retardant MDF is typically red or blue
Although similar manufacturing processes are used in making all types of fibreboard, MDF has a typical density of 600–800 kg/m³ or 0.022–0.029 lb/in3, in contrast to particle board (160–450 kg/m³) and to high-density fibreboard (600–1,450 kg/m³).
In Australia and New Zealand, the main species of tree used for MDF is plantation-grown radiata pine; but a variety of other products have also been used, including other woods, waste paper and fibres. Where moisture resistance is desired, a proportion of eucalypt species may be used, making use of the endemic oil content of such trees.
The trees are debarked after being cut. The bark can be sold for use in landscaping, or burned in on-site furnaces. The debarked logs are sent to the MDF plant, where they go through the chipping process. A typical disk chipper contains 4–16 blades. Any resulting chips that are too large may be re-chipped; undersized chips may be used as fuel. The chips are then washed and checked for defects. Chips may be stored in bulk, as a reserve for manufacturing.
Compared to other fibre boards, such as Masonite, MDF is characterised by the next part of the process, and how the fibres are processed as individual, but intact, fibres and vessels, manufactured through a dry process. The chips are then compacted into small plugs using a screw feeder, heated for 30–120 seconds to soften the lignin in the wood, then fed into a defibrator. A typical defibrator comprises two counter-rotating discs with grooves in their faces. Chips are fed into the centre and are fed outwards between the discs by centrifugal force. The decreasing size of the grooves gradually separates the fibres, aided by the softened lignin between them.
From the defibrator, the pulp enters a 'blowline', a distinctive part of the MDF process. This is an expanding circular pipeline, initially 40 mm in diameter, increasing to 1500 mm. Wax is injected in the first stage, which coats the fibres and is distributed evenly by the turbulent movement of the fibres. A urea-formaldehyde resin is then injected as the main bonding agent. The wax improves moisture resistance and the resin initially helps reduce clumping. The material dries quickly in the final heated expansion chamber of the blowline and expands into a fine, fluffy and lightweight fibre. This fibre may be used immediately, or stored.
Dry fibre gets sucked into the top of a 'pendistor', which evenly distributes fibre into a uniform mat below it, usually of 230–610 mm thickness. The mat is pre-compressed and either sent straight to a continuous hot press or cut into large sheets for a multi-opening hot press. The hot press activates the bonding resin and sets the strength and density profile. The pressing cycle operates in stages, with the mat thickness being first compressed to around 1.5× the finished board thickness, then compressed further in stages and held for a short period. This gives a board profile with zones of increased density, thus mechanical strength, near the two faces of the board and a less dense core.
After pressing, MDF is cooled in a star dryer or cooling carousel, trimmed and sanded. In certain applications, boards are also laminated for extra strength.
The environmental impact of MDF has greatly improved over the years. Today, many MDF boards are made from a variety of materials. These include other woods, scrap, recycled paper, bamboo, carbon fibres and polymers, forest thinnings and sawmill off-cuts.
As manufacturers are being pressured to come up with greener products, they have started testing and using non-toxic binders. New raw materials are being introduced. Straw and bamboo are becoming popular fibres because they are a fast-growing renewable resource.
Comparison with natural woodsEdit
MDF does not contain knots or rings, making it more uniform than natural woods during cutting and in service. However, MDF is not entirely isotropic, since the fibres are pressed tightly together through the sheet. Typical MDF has a hard, flat, smooth surface that makes it ideal for veneering, as there is no underlying grain to telegraph through the thin veneer as with plywood. A so-called "Premium" MDF is available that features more uniform density throughout the thickness of the panel.
MDF may be glued, doweled or laminated. Typical fasteners are T-nuts and pan-head machine screws. Smooth-shank nails do not hold well, and neither do fine-pitch screws, especially in the edge. Special screws are available with a coarse thread pitch, but sheet-metal screws also work well. Like natural wood, MDF may split when woodscrews are installed without pilot holes.
- Is an excellent substrate for veneers.
- Some varieties are less expensive than many natural woods
- Isotropic (its properties are the same in all directions as a result of having no grain), so no tendency to split
- Consistent in strength and size
- Shapes well.
- Stable dimensions (won't expand or contract like wood)
- Easy to finish (i.e., paint)
- Denser than plywood or chipboard (the resins are heavy)
- Low grade MDF may swell and break when saturated with water.
- May warp or expand if not sealed.
- May release formaldehyde, which is a known human carcinogen and may cause allergy, eye and lung irritation when cutting and sanding
- Dulls blades more quickly than many woods. Use of tungsten carbide edged cutting tools is almost mandatory, as high speed steel dulls too quickly.
- Though it does not have a grain in the plane of the board, it does have one into the board. Screwing into the edge of a board will generally cause it to split in a fashion similar to delaminating.
- Subject to significant shrinkage in low humidity environments.
- Trim (e.g. baseboards) comes pre-primed, but this is insufficient for fine finish painting. Painting with latex paints is difficult due to rapid water absorption. Most finishes appear uneven and nail holes tend to pucker.
MDF is often used in school projects because of its flexibility. Slatwall Panels made from MDF are used in the shop fitting industry. MDF is primarily used for internal use applications due to its poor moisture resistance. it is available in raw form with fine sanded surface or with decorative overlay.
MDF is also usable for furniture such as cabinets, because of its strong surface.
When MDF is cut, a large quantity of dust particles are released into the air. It's important a respirator is worn and that the material is cut in a controlled and ventilated environment. It's good practice to seal exposed edges to limit emissions from binders contained in this material.
Formaldehyde resins are commonly used to bind together the fibres in MDF, and testing has consistently revealed that MDF products emit free formaldehyde and other volatile organic compounds that pose health risks at concentrations considered unsafe, for at least several months after manufacture. Urea-formaldehyde is always being slowly released from the edges and surface of MDF. When painting, it is a good idea to coat all sides of the finished piece in order to seal in the free formaldehyde. Wax and oil finishes may be used as finishes but they are less effective at sealing in the free formaldehyde.
Whether these constant emissions of formaldehyde reach harmful levels in real-world environments is not yet fully determined. The primary concern is for the industries using formaldehyde. As far back as 1987, the U.S. EPA classified it as a "probable human carcinogen" and, after more studies, the WHO International Agency for Research on Cancer (IARC), in 1995, also classified it as a "probable human carcinogen". Further information and evaluation of all known data led the IARC to reclassify formaldehyde as a "known human carcinogen" associated with nasal sinus cancer and nasopharyngeal cancer, and possibly with leukaemia in June 2004.
According to International Composite Board Emission Standards (ICBES), there are 3 European formaldehyde classes, namely: E0, E1 and E2. This classification is based on the measurement of formaldehyde emission levels. For instance, E0 is classified as having less than 3 milligrams of formaldehyde out of every 100 grams of the glue used in particleboard and plywood fabrication. E1 and E2, conversely, are classified as having 9 and 30 grams of formaldehyde per 100 grams of glue respectively. All around the world variable certification and labeling schemes are there for such products that can be explicit to formaldehyde release, like that of Californian Air Resources Board (CARB).
Veneered MDF provides many of the advantages of MDF with a decorative wood veneer surface layer. In modern construction, spurred by the high costs of hardwoods, manufacturers have been adopting this approach to achieve a high quality finishing wrap covering over a standard MDF board. One common type uses oak veneer. Making veneered MDF is a complex procedure, which involves taking an extremely thin slice of hardwood (approx 1-2mm thick) and then through high pressure and stretching methods wrapping them around the profiled MDF boards. This is only possible with very simple profiles because otherwise when the thin wood layer has dried out, it will break at the point of bends and angles.
- Spence, William P. (2005). The Home Carpenters & Woodworker's Repair Manual. New York City: Sterling. ISBN 1-4027-1055-0 p. 114
- "Medium Density Fiberboard, Moulding, Embossing, Kitchen Cabinets – Composite Panel Association". Decorativesurfaces.org. Retrieved 2014-04-02.
- United Nations (2005). European forest sector outlook study: 1960/2000/2020, main report. New York [u.a.]: United Nations. p. 32. ISBN 9211169216.
- R. Kozlowski and M. Helwig (December 1996). HTTPS Look on Cellulose Modification. Proceedings of the International Symposium on Cellulose Modification. Honolulu, USA.
- ANSI A208.2 MDF for Interior Applications (PDF). Gaithersburg, MD: Composite Panel Association. 2002. p. 3.
- "MDF, LDF, HDF - www.sppd.pl". Sppd.pl. Retrieved 17 January 2018.
- "The Manufacturing Process". Medium Density Fibreboard. Dept. Forestry, Australian National University.
- "Medium Density Fibreboard". Design-technology.org. Retrieved 2014-04-02.
- "MDF Board FAQ - Tutorial". Diyaudioandvideo.com. Retrieved 2014-04-02.
- "IARC Monographs on the Evaluation of Carcinogenic Risks to Humans Volume 88 (2006) Formaldehyde, 2-Butoxyethanol and 1-tert-Butoxypropan-2-ol". WHO Press. 2006.
- "An Introduction to Indoor Air Quality", United States Environmental Protection Agency
- "Medium Density Fibreboard". Design-technology.org. Retrieved 2016-12-14.
- George E. Myers. "Effects of post-manufacture board treatments on formaldehyde emission : a literature review (1960-1984)" (PDF). Fpl.fs.fed.us. Retrieved 17 January 2018.
- Hodgson, A. T.; Beal, D.; McIlvaine, J. E. R. (1 December 2002). "Sources of formaldehyde, other aldehydes and terpenes in a new manufactured house". Indoor Air. 12 (4): 235–242. doi:10.1034/j.1600-0668.2002.01129.x. Retrieved 17 January 2018 – via Wiley Online Library.
- "ALDEHYDE EMISSIONS FROM PARTICLEBOARD AND MEDIUM DENSITY FIBERBOARD PRODUCTS" (PDF). Fpl.fs.fed.us. Retrieved 17 January 2018.
- "Formaldehyde and Cancer Risk". National Cancer Institute. Retrieved 17 January 2018.
- "Which Particleboard and Plywood Standard Should you Use?". Amrosia.com. Retrieved 17 January 2018.
- "Veneered MDF". Skirtingboard.co.uk. Retrieved 2014-04-02.
- English, Brent, John A. Youngquist, and Andrzej M. Krzysik, Lignocellulosic Composites in Gilbert, Richard D., ed. Cellulosic polymers, blends and composites. New York: Hanser Publishers: 115–130; 1994. Chapter 6