Carrier generation and recombination
In the solid-state physics of semiconductors, carrier generation and carrier recombination are processes by which mobile charge carriers (electrons and electron holes) are created and eliminated. Carrier generation and recombination processes are fundamental to the operation of many optoelectronic semiconductor devices, such as photodiodes, light-emitting diodes and laser diodes. They are also critical to a full analysis of p-n junction devices such as bipolar junction transistors and p-n junction diodes.
The electron–hole pair is the fundamental unit of generation and recombination in inorganic semiconductors, corresponding to an electron transitioning between the valence band and the conduction band where generation of electron is a transition from the valence band to the conduction band and recombination leads to a reverse transition.
- 1 Overview
- 2 Relation between generation and recombination
- 3 Carrier generation
- 4 Recombination mechanisms
- 5 Radiative Recombination
- 6 Non-radiative recombination
- 7 References
- 8 Further reading
- 9 External links
Like other solids, semiconductor materials have an electronic band structure determined by the crystal properties of the material. Energy distribution among electrons is described by the Fermi level and the temperature of the electrons. At absolute zero temperature, all of the electrons have energy below the Fermi level; but at non-zero temperatures the energy levels are filled following a Boltzmann distribution.
In undoped semiconductors the Fermi level lies in the middle of a forbidden band or band gap between two allowed bands called the valence band and the conduction band. The valence band, immediately below the forbidden band, is normally very nearly completely occupied. The conduction band, above the Fermi level, is normally nearly completely empty. Because the valence band is so nearly full, its electrons are not mobile, and cannot flow as electric current.
However, if an electron in the valence band acquires enough energy to reach the conduction band (as a result of interaction with other electrons, holes, photons, or the vibrating crystal lattice itself), it can flow freely among the nearly empty conduction band energy states. Furthermore, it will also leave behind a hole that can flow as current exactly like a physical charged particle.
Carrier generation describes processes by which electrons gain energy and move from the valence band to the conduction band, producing two mobile carriers; while recombination describes processes by which a conduction band electron loses energy and re-occupies the energy state of an electron hole in the valence band.
These processes must conserve both quantized energy and momentum, and the vibrating lattice plays a large role in conserving momentum as, in collisions, photons can transfer very little momentum in relation to their energy.
Relation between generation and recombinationEdit
Recombination and generation are always happening in semiconductors, both optically and thermally. As predicted by thermodynamics, a material at thermal equilibrium will have generation and recombination rates that are balanced so that the net charge carrier density remains constant. The resulting probability of occupation of energy states in each energy band is given by Fermi–Dirac statistics.
The product of the electron and hole densities ( and ) is a constant at equilibrium, maintained by recombination and generation occurring at equal rates. When there is a surplus of carriers (i.e., ), the rate of recombination becomes greater than the rate of generation, driving the system back towards equilibrium. Likewise, when there is a deficit of carriers (i.e., ), the generation rate becomes greater than the recombination rate, again driving the system back towards equilibrium. As the electron moves from one energy band to another, the energy and momentum that it has lost or gained must go to or come from the other particles involved in the process (e.g. photons, electron, or the system of vibrating lattice atoms).
When light interacts with a material, it can either be absorbed (generating a pair of free carriers or an exciton) or it stimulate a recombination event. The generated photon has similar properties to the one responsible for the event. Absorption is the active process in photodiodes, solar cells and other semiconductor photodetectors, while stimulated emission is the principle of operation in laser diodes.
When light with sufficient energy hits a semiconductor, it can excite electrons across the band gap. This generates additional charge carriers, temporarily lowering the electrical resistance of materials. This higher conductivity in the presence of light is known as photoconductivity. This conversion of light into electricity is widely used in photodiodes.
Carrier recombination can happen through multiple relaxation channels. The main ones are band-to-band recombination, Shockley–Read–Hall (SRH)
trap-assisted recombination, Auger recombination and surface recombination. These decay channels can be separated into radiative and non-radiative. The latter occurs when the excess energy is converted into heat by phonon emission after the mean lifetime , whereas in the former at least part of the energy is released by light emission or luminescence after a radiative lifetime . The carrier lifetime is then obtained from the rate of both type of events according to: 
From which we can also define the internal quantum efficiency or quantum yield, as:
Band-to-band radiative recombinationEdit
Band-to-band recombination is the name for the process of electrons jumping down from the conduction band to the valence band in a radiative manner. During band-to-band recombination, a form of spontaneous emission, the energy absorbed by a material is released in the form of photons. Generally these photon contain the same or less energy than the one initially absorbed. This effect is how LEDs create light. Because the photon carries relatively little momentum, radiative recombination is significant only in direct bandgap materials. This process is also known as bimolecular recombination.
This type of recombination depends on the density of electrons and holes in the excited state, denoted by and respectively. Let us represent the carrier generation rate as and the radiative recombination as . Then considering the case in which only band-to-band recombination occurs we can express the change in carrier density as a function of time as:
where is called the radiative recombination rate, is the intrinsic carrier density, and are the equilibrium carrier densities. In the presence of electron hole pairs, the charge neutrality remains and the non-equilibrium densities are given by :
Solving this equation by considering charge neutrality, the radiative lifetime is then given by
Stimulated emission is a process in which an incident photon interacts with an excited electron causing it to recombine and emit a photon with the same properties of the incident one, in terms of phase, frequency, polarization, and direction of travel. Stimulated emission together with the principle of population inversion are at the hearth of operation of lasers and masers. It has been shown by Einstein at the beginning of the twentieth century that if the excited and the ground level are non degenerate then the absorption rate and the stimulated emission rate are the same. Else if level 1 and level 2 are -fold and -fold degenerate respectively, the new relation is:
Non-radiative recombination is a process in phosphors and semiconductors, whereby charge carriers recombine with releasing phonon instead of photons. Non-radiative recombination in optoelectronics and phosphors is an unwanted process, lowering the light generation efficiency and increasing heat losses.
Non-radiative life time is the average time before an electron in the conduction band of a semiconductor recombines with a hole. It is an important parameter in optoelectronics where radiative recombination is required to produce a photon; if the non-radiative life time is shorter than the radiative, a carrier is more likely to recombine non-radiatively. This results in low internal quantum efficiency.
In Shockley-Read-Hall recombination (SRH), also called trap-assisted recombination, the electron in transition between bands passes through a new energy state (localized state) created within the band gap by a dopant or a defect in the crystal lattice; such energy states are called traps. Non-radiative recombination occurs primarily at such sites. The energy is exchanged in the form of lattice vibration, a phonon exchanging thermal energy with the material.
Since traps can absorb differences in momentum between the carriers, SRH is the dominant recombination process in silicon and other indirect bandgap materials. However, trap-assisted recombination can also dominate in direct bandgap materials under conditions of very low carrier densities (very low level injection) or in materials with high density of traps such as Perovskites. The process is named after William Shockley, William Thornton Read and Robert N. Hall.who published it in 1962.
Types of trapsEdit
Electron traps vs. hole trapsEdit
Even though all the recombination events can be described in terms of electron movements, it is common to visualize the different processes in terms of excited electron and the electron holes they leave behind. In this context, if trap levels are close to the conduction band, they can temporarily immobilize excited electrons or in other words, they are electron traps. On the other hand, if their energy lies close to the valence band they become hole traps.
Shallow traps vs. deep trapsEdit
The distinction between shallow and deep traps is commonly made depending on how close electron traps are to the conduction band and how close hole traps are to the valence band. If the difference between trap and band is smaller than the thermal energy kBT it is often said that it is a shallow trap. Alternatively, if the difference is larger than the thermal energy, it is called a deep trap. This difference is useful because shallow traps can be emptied more easily and thus are often not as detrimental to the performance of optoelectronic devices.
In the SRH model, four things can happen involving trap levels:
- An electron in the conduction band can be trapped in an intragap state.
- An electron can be emitted into the conduction band from a trap level.
- An electron hole in the valence band can be captured by a trap. This is analogous to a filled trap releasing an electron into the valence band.
- A captured hole can be released into the valence band. Analogous to the capture of an electron from the valence band.
Where is the density of trap states and is the probability of that occupied state. Considering a material containing both types of traps, we can define two trapping coefficients and two de-trapping coeficients . In equilibrium, both trapping and de-trapping should be balanced ( and ). Then, the four rates as a function of become:
Where and are the electron and hole densities when the quasi Fermi level matches the trap energy.
In steady-state condition, the net trapping rate of electrons should match the net recombination rate for holes, in other words: . This eliminates the occupation probability and leads to the Shockley-Read-Hall expression for the trap-assisted recombination:
Where the average lifetime for electrons and holes are defined as:
In Auger recombination the energy is given to a third carrier which is excited to a higher energy level without moving to another energy band. After the interaction, the third carrier normally loses its excess energy to thermal vibrations. Since this process is a three-particle interaction, it is normally only significant in non-equilibrium conditions when the carrier density is very high. The Auger effect process is not easily produced, because the third particle would have to begin the process in the unstable high-energy state.
In thermal equilibrium the Auger recombination and thermal generation rate equal each other
where are the Auger capture probabilities. The non-equilibrium Auger recombination rate and resulting net recombination rate under steady-state conditions are
The Auger lifetime is given by
The mechanism causing LED efficiency droop was identified in 2007 as Auger recombination, which met with a mixed reaction. In 2013, an experimental study claimed to have identified Auger recombination as the cause of efficiency droop. However, it remains disputed whether the amount of Auger loss found in this study is sufficient to explain the droop. Other frequently quoted evidence against Auger as the main droop causing mechanism is the low-temperature dependence of this mechanism which is opposite to that found for the drop.
Trap-assisted recombination at the surface of a semiconductor is referred to as surface recombination. This occurs when traps at or near the surface or interface of the semiconductor form due to dangling bonds caused by the sudden discontinuation of the semiconductor crystal. Surface recombination is characterized by surface recombination velocity which depends on the density of surface defects. In applications such as solar cells, surface recombination may be the dominant mechanism of recombination due to the collection and extraction of free carriers at the surface. In some applications of solar cells, a layer of transparent material with a large band gap, also known as a window layer, is used to minimize surface recombination. Passivation techniques are also employed to minimize surface recombination.
- Elhami Khorasani, Arash; Schroder, Dieter K.; Alford, T. L. (2014). "Optically Excited MOS-Capacitor for Recombination Lifetime Measurement". IEEE Electron Device Letters. 35 (10): 986–988. Bibcode:2014IEDL...35..986K. doi:10.1109/LED.2014.2345058.
- Pelant, Ivan; Valenta, Jan (2012-02-09), "Luminescence of disordered semiconductors", Luminescence Spectroscopy of Semiconductors, Oxford University Press, pp. 242–262, doi:10.1093/acprof:oso/9780199588336.003.0009, ISBN 9780199588336
- Stranks, Samuel D.; Burlakov, Victor M.; Leijtens, Tomas; Ball, James M.; Goriely, Alain; Snaith, Henry J. (2014-09-11). "Recombination Kinetics in Organic-Inorganic Perovskites: Excitons, Free Charge, and Subgap States". Physical Review Applied. 2 (3): 034007. doi:10.1103/PhysRevApplied.2.034007.
- Li, Sheng S., ed. (2006). Semiconductor Physical Electronics. p. 140. doi:10.1007/0-387-37766-2. ISBN 978-0-387-28893-2.
- NISOLI, MAURO. (2016). SEMICONDUCTOR PHOTONICS. SOCIETA EDITRICE ESCULAPI. ISBN 978-8893850025. OCLC 964380194.
- Svelto. (1989). Principles of Lasers ... p. 3. OCLC 249201544.
- Shockley, W.; Read, W. T. (1 September 1952). "Statistics of the Recombinations of Holes and Electrons". Physical Review. 87 (5): 835–842. Bibcode:1952PhRv...87..835S. doi:10.1103/PhysRev.87.835.
- Hall, R.N. (1951). "Germanium rectifier characteristics". Physical Review. 83 (1): 228.
- NISOLI, MAURO. (2016). SEMICONDUCTOR PHOTONICS. SOCIETA EDITRICE ESCULAPI. ISBN 978-8893850025. OCLC 964380194.
- Kandada, Ajay Ram Srimath; D'Innocenzo, Valerio; Lanzani, Guglielmo; Petrozza, Annamaria (2016), Da Como, Enrico; De Angelis, Filippo; Snaith, Henry; Walker, Alison (eds.), "Chapter 4. Photophysics of Hybrid Perovskites", Unconventional Thin Film Photovoltaics, Royal Society of Chemistry, pp. 107–140, doi:10.1039/9781782624066-00107, ISBN 9781782622932
- Li, Sheng S., ed. (2006). Semiconductor Physical Electronics. p. 143. doi:10.1007/0-387-37766-2. ISBN 978-0-387-28893-2.
- Li, Sheng S., ed. (2006). Semiconductor Physical Electronics. p. 144. doi:10.1007/0-387-37766-2. ISBN 978-0-387-28893-2.
- Stevenson, Richard (August 2009) The LED’s Dark Secret: Solid-state lighting won't supplant the lightbulb until it can overcome the mysterious malady known as droop. IEEE Spectrum
- Justin Iveland; Lucio Martinelli; Jacques Peretti; James S. Speck; Claude Weisbuch. "Cause of LED Efficiency Droop Finally Revealed". Physical Review Letters, 2013. Science Daily. Retrieved 23 April 2013.
- Nelson, Jenny (2003). The Physics of Solar Cells. London: Imperial College Press. p. 116. ISBN 978-1-86094-340-9.
- Eades, W.D.; Swanson, R.M. (1985). "Calculation of surface generation and recombination velocities at the Si-SiO2 interface". Journal of Applied Physics. 58 (11): 4267–4276. doi:10.1063/1.335562. ISSN 0021-8979.
- N.W. Ashcroft and N.D. Mermin, Solid State Physics, Brooks Cole, 1976