Composite armour(Redirected from Composite armor)
This article needs additional citations for verification. (September 2009) (Learn how and when to remove this template message)
Composite armour is a type of vehicle armour consisting of layers of different material such as metals, plastics, ceramics or air. Most composite armours are lighter than their all-metal equivalent, but instead occupy a larger volume for the same resistance to penetration. It is possible to design composite armour stronger, lighter and less voluminous than traditional armour, but the cost is often prohibitively high, restricting its use to especially vulnerable parts of a vehicle. Its primary purpose is to help defeat high explosive anti-tank (HEAT) rounds.
HEAT had posed a serious threat to armoured vehicles since its introduction in World War II. Lightweight and small, HEAT rounds could nevertheless penetrate hundreds of millimetres of the hardest steel armours. The capability of most materials for defeating HEAT follows the "density law", which states that the penetration of shaped charge jets is proportional to the square root of the shaped charge liner density (typically copper) divided by the square root of the target density. On a weight basis, lighter targets are more advantageous than heavier targets, but using large quantities of lightweight materials has obvious disadvantages in terms of mechanical layout. Certain materials have an optimal compromise in terms of density that makes them particularly useful in this role.
The earliest known composite armour for armoured vehicles was developed as part of the US Army's T95 experimental series from the mid-1950s. The T95 featured "siliceous-cored armor" which contained a plate of fused silica glass between rolled steel plates. The stopping power of glass exceeds that of steel armour on a thickness basis and in many cases glass is more than twice as effective as steel on a thickness basis. Although the T95 never entered production, a number of its concepts were used on the M60 Patton, and during the development stage (as the XM60) the siliceous-cored armour was at least considered for use, although it was not a feature of the production vehicles.
This article needs attention from an expert in Military history/Military science and technology task force.(September 2009)
The first widespread use of a composite armour appears to have been on the Soviet T-64. It used an armour known as Combination K, which apparently is glass-reinforced plastic sandwiched between inner and outer steel layers. Through a mechanism called thixotropy, the resin changes to a fluid under constant pressure, allowing the armour to be moulded into curved shapes. Later models of the T-64, along with newer designs, used a boron carbide-filled resin aggregate for greatly improved protection. The Soviets also invested heavily in reactive armour, which allowed them some ability to control quality, even after production.
The most common type of composite armour today is Chobham armour, first developed and used by the British in the experimental FV 4211 tank, which was based on Chieftain tank components. Chobham sandwiches a layer of ceramic between two plates of steel armour, which was shown to dramatically increase the resistance to HEAT rounds, even in comparison to other composite armour designs. Chobham was such an improvement that it was soon used on the new U.S. M1 Abrams main battle tank (MBT) as well. It is the fabrication of the ceramic in large tiles that gives the Challenger and Abrams their "slab sided" look.
Chobham's precise mechanism for defeating HEAT was uncovered in the 1980s. High speed photography showed that the ceramic material shatters as the HEAT round penetrates, the highly energetic fragments destroying the geometry of the metal jet generated by the hollow shaped charge, greatly diminishing the penetration. The effectiveness of the system was amply demonstrated in Desert Storm, where not a single British Army Challenger tank was lost to enemy tank fire. (However, one was destroyed by friendly fire on March 25, 2003, killing two crew members after a HESH round detonated on the commander's hatch causing high-velocity fragments to enter the turret.) Chobham-type armour is currently in its third generation and is used on modern western tanks such as the British Challenger 2 and the American M1 Abrams.
The Japanese Type 10 and Type 90 Kyū-maru MBTs, French Leclerc, Iranian Karrar,Turkish Altay, Indian Arjun, Italian Ariete and Chinese Type 96/98 and Type 99 tanks use modular composite armour. The adoption of Modular composite armour design facilitated upgrading and exchange of the armour.
Soviet/Russian T-80Us and the Chinese Type 96 use composite armour in tandem with explosive reactive armour (ERA), making it hard for missiles and tank rounds to penetrate the frontal and a portion of their side armour.
Composite armour has since been applied to smaller vehicles, right down to jeep-sized. Many of these systems are applied as upgrades to existing armour, which makes them difficult to place around the entire vehicle. Nevertheless, they are often surprisingly effective; upgrades with MEXAS ceramic armour to Canadian M113s were carried out in the 1990s, after it was realized that it would offer more protection than newly built IFVs like the M2 Bradley.
In 2004, Marvin Heemeyer used an ad hoc composite armour on his Komatsu D355A bulldozer ("Killdozer") used in a rampage in response to a dispute with the city he lived in over a zoning issue. The armour, at some places a foot thick, consisted of a layer of concrete sandwiched between layers of steel, successfully rendering the vehicle impervious to small arms fire and small explosives.
- Evaluation of Siliceous Cored Armor for the XM60 Tank Archived June 5, 2011, at the Wayback Machine.
- "UK Ministry of Defence : Army Board of Inquiry Report" (PDF). Archived from the original (PDF) on 2012-10-26. Retrieved 2016-07-06.