Fused glass is glass that has been fired (heat-processed) in a kiln at a range of high temperatures from 593 °C (1,099 °F) to 816 °C (1,501 °F). There are 3 main distinctions for temperature application and the resulting effect on the glass.
Firing in the lower ranges of these temperatures 593–677 °C (1099–1251 °F) is called slumping. Firing in the middle ranges of these temperatures 677–732 °C (1251–1350 °F) is considered "tack fusing". Firing the glass at the higher spectrum of this range 732–816 °C (1350–1501 °F) is a "full fuse".
All of these techniques can be applied to one glass work in separate firings to add depth, relief and shape.
While the precise origins of glass fusing techniques are not known with certainty, there is archeological evidence that the Egyptians were familiar with techniques ca. 2000 BCE. Although this date is generally accepted by researchers, some historians argue that the earliest fusing techniques were first developed by the Romans, who were much more prolific glassworkers. Fusing was the primary method of making small glass objects for approximately 2,000 years, until the development of the glass blowpipe. Glassblowing largely supplanted fusing due to its greater efficiency and utility.
While glass working in general enjoyed a revival during the Renaissance, fusing was largely ignored during this period. Fusing began to regain popularity in the early part of the 20th century, particularly in the U.S. during the 1960s. Modern glass fusing is a widespread hobby but the technique is also gaining popularity in the world of fine art.
Types of glass
When glass is fused, unless the separate pieces are of the same COE (co-efficient-of-expansion) the pieces will shatter as the different types of glass cool, as not being the same COE will cause them to contract at differing rates, causing stress fractures to appear between the pieces fused together. Many companies make glass of the same COE, such as the Spectrum glass system 96, which has also been adopted by other manufacturers so that glass from different companies can be used in the same piece without fear of destruction. Frit (graded glass fragments) are also subject to differing rates of expansion and can also cause a piece to fail. The best way to ensure that frit will be compatible with the rest of the glass is to make your own from the same glass as the base section of the work. The stress in a piece of work can be observed by placing the item between two polarizing filters. This will show any area of tension that may be problematic.
Most contemporary fusing methods involve stacking, or layering thin sheets of glass, often using different colors to create patterns or simple images. The stack is then placed inside the kiln (which is almost always electric, but can be heated by gas or wood) and then heated through a series of ramps (rapid heating cycles) and soaks (holding the temperature at a specific point) until the separate pieces begin to bond together. The longer the kiln is held at the maximum temperature, the more thoroughly the stack will fuse, eventually softening and rounding the edges of the original shape. Once the desired effect has been achieved at the maximum desired temperature, the kiln temperature will be brought down quickly through the temperature range of 815 °C (1,499 °F) to 573 °C (1,063 °F) to avoid devitrification. The glass is then allowed to cool slowly over a specified time, soaking at specified temperature ranges which are essential to the annealing process. This prevents uneven cooling and breakage and produces a strong finished product.
This cooling takes place normally for a period of 10–12 hours in 3 stages.
The first stage- the rapid cool period is meant to place the glass into the upper end of the annealing range 516 °C (961 °F). The second stage- the anneal soak at 516 °C (961 °F) is meant to equalize the temperature at the core and the surface of the glass at 516 °C (961 °F) relieving the stress between those areas. The last stage, once all areas have had time to reach a consistent temperature, is the final journey to room temperature. The kiln is slowly brought down over the course of 2 hours to 371 °C (700 °F), soaked for 2 hours at 371 °C (700 °F), down again to 260 °C (500 °F) which ends the firing schedule. The glass will remain in the closed kiln until the pyrometer reads room temperature.
Note that these temperatures are not hard and fast rules. Depending on the kiln, the size of the project, the number of layers, the desired finished look, and even the brand of glass, ramp and soak temperatures and times may vary. Small pendants can be fired and cooled very rapidly. For instance, small glass pieces can be fired in as little as one hour. According to Paragon Industries, the QuikFire can reach 537 °C (999 °F) in five minutes.
Fused glass techniques are generally used to create Art glass, glass tiles, and jewellery, notably beads. Slumping techniques allow the creation of larger, functional pieces like dishes, bowls, plates, and ashtrays. Producing functional pieces generally requires 2 or more separate firings, one to fuse the glass and a second slump it to shape.
Since the 1970s, more hobbyists have focused on using kiln-fused glass to make beads and components for jewellery. This has become especially popular since the introduction of glass manufactured for the specific purpose of fusing in a kiln.